| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | CRH | HRA | CRH | ||||
| 86,6 | 70,0 | 1037 | 78,5 | 55,0 | 599 | ||
| 86,3 | 69,5 | 1017 | 78.2 | 54,5 | 589 | ||
| 86.1 | 69,0 | 997 | 77,9 | 54,0 | 579 | ||
| 85,8 | 68,5 | 978 | 77,7 | 53,5 | 570 | ||
| 85,5 | 68,0 | 959 | 77,4 | 53,0 | 561 | ||
| 85,2 | 67,5 | 941 | 77.1 | 52,5 | 551 | ||
| 85,0 | 67,0 | 923 | 76,9 | 52,0 | 543 | ||
| 84,7 | 66,5 | 906 | 76,6 | 51,5 | 534 | ||
| 84,4 | 66,0 | 889 | 501 | 76,3 | 51,0 | 525 | |
| 84.1 | 65,5 | 872 | 494 | 76.1 | 50,5 | 517 | |
| 83,9 | 65,0 | 856 | 488 | 75,8 | 50,0 | 509 | |
| 83,6 | 64,5 | 840 | 481 | 75,5 | 49,5 | 501 | |
| 83,3 | 64,0 | 825 | 474 | 75.3 | 49,0 | 493 | |
| 83.1 | 63,5 | 810 | 468 | 75,0 | 48,5 | 485 | |
| 82,8 | 63,0 | 795 | 461 | 74,7 | 48,0 | 478 | |
| 82,5 | 62,5 | 780 | 455 | 74,5 | 47,5 | 470 | |
| 82,2 | 62,0 | 766 | 449 | 74.2 | 47,0 | 463 | |
| 82,0 | 61,5 | 752 | 442 | 73,9 | 46,5 | 456 | |
| 81,7 | 61,0 | 739 | 436 | 73,7 | 46,0 | 449 | |
| 81,4 | 60,5 | 726 | 430 | 73,4 | 45,5 | 443 | |
| 81.2 | 60,0 | 713 | 424 | 73.2 | 45,0 | 436 | |
| 80,9 | 59,5 | 700 | 418 | 72,9 | 44,5 | 429 | |
| 80,6 | 59,0 | 688 | 413 | 72,6 | 44,0 | 423 | |
| 80,3 | 58,5 | 676 | 407 | 72,4 | 43,5 | 417 | |
| 80,1 | 58,0 | 664 | 401 | 72.1 | 43,0 | 411 | |
| 79,8 | 57,5 | 653 | 396 | 71,8 | 42,5 | 405 | |
| 79,5 | 57,0 | 642 | 391 | 71,6 | 42,0 | 399 | |
| 79,3 | 56,5 | 631 | 385 | 71.3 | 41,5 | 393 | |
| 79,0 | 56,0 | 620 | 380 | 71.1 | 41,0 | 388 | |
| 78,7 | 55,5 | 609 | 375 | 70,8 | 40,5 | 382 | |
Tableau de conversion des valeurs de dureté des matériaux en métaux ferreux
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | CRH | HRA | CRH | ||||
| 370 | 70,5 | 40,0 | 377 | 269 | 28,0 | 274 | |
| 365 | 70.3 | 39,5 | 372 | 266 | 27,5 | 271 | |
| 360 | 70,0 | 39,0 | 367 | 263 | 27,0 | 268 | |
| 355 | 38,5 | 362 | 260 | 26,5 | 264 | ||
| 350 | 38,0 | 351 | 257 | 26,0 | 261 | ||
| 345 | 37,5 | 352 | 254 | 25,5 | 258 | ||
| 341 | 37,0 | 347 | 251 | 25,0 | 255 | ||
| 336 | 36,5 | 342 | 248 | 24,5 | 252 | ||
| 332 | 36,0 | 338 | 245 | 24,0 | 249 | ||
| 327 | 35,5 | 333 | 242 | 23,5 | 246 | ||
| 323 | 35,0 | 329 | 240 | 23,0 | 243 | ||
| 318 | 34,5 | 324 | 237 | 22,5 | 240 | ||
| 314 | 34,0 | 320 | 234 | 22,0 | 237 | ||
| 310 | 33,5 | 316 | 232 | 21,5 | 234 | ||
| 306 | 33,0 | 312 | 229 | 21,0 | 231 | ||
| 302 | 32,5 | 308 | 227 | 20,5 | 229 | ||
| 298 | 32,0 | 304 | 225 | 20,0 | 226 | ||
| 294 | 31,5 | 300 | 222 | 19,5 | 223 | ||
| 291 | 31,0 | 296 | 220 | 19,0 | 221 | ||
| 287 | 30,5 | 292 | 218 | 18,5 | 218 | ||
| 283 | 30,0 | 289 | 216 | 18,0 | 216 | ||
| 280 | 29,5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29,0 | 281 | 211 | 17,0 | 211 | ||
| 273 | 28,5 | 278 | |||||
Note:
1. Dureté Brinell : Elle est principalement utilisée pour mesurer la dureté des pièces moulées, des pièces forgées, des pièces en métaux non ferreux, des billettes laminées à chaud et des pièces recuites. La plage de mesure est ≥HB450.
2. Dureté Rockwell : HRA est principalement utilisé pour les échantillons de haute dureté afin de mesurer la dureté de surface des matériaux et des surfaces dont la dureté est supérieure à HRC67, tels que le carbure cémenté, l'acier nitruré, etc. La plage de mesure est HRA>70. HRC est principalement utilisé pour mesurer la dureté des pièces en acier (telles que l'acier au carbone, l'acier à outils, l'acier allié, etc.) après trempe ou revenu. La plage de mesure est HRC20~67.
3. Dureté Vickers : utilisée pour mesurer la dureté des pièces minces et des pièces en tôle d'acier, et peut également être utilisée pour mesurer la dureté des pièces durcies en surface telles que la cémentation, la cyanuration et la nitruration.